| About |
|---|
| Conductive NORYL GTX resin designed for profile extrusion. This grade can be electrostatic or powder coat painted without the need for a primer. In addition, its high heat capability allows it to be painted on the same line as metal.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | Sprayable,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 7.8 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.3 to 1.5 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 4.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.40 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2420 | MPa | ASTM D638 |
| — | 2670 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| yield | 66.0 | MPa | ISO 527-2/50 |
| fracture | 63.0 | MPa | ASTM D638 |
| fracture | 64.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.8 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 6.1 | % | ASTM D638 |
| fracture | 7.1 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2520 | MPa | ASTM D790 |
| — | 2470 | MPa | ISO 178 |
| bending strength | |||
| — | 103 | MPa | ISO 178 |
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 58 | J/m | ASTM D256 |
| 23℃ | 110 | J/m | ASTM D256 |
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 5.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 187 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 184 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| B50 | 197 | ℃ | ASTM D1525 10 , ISO 306/B50 10 |
| B120 | 198 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.6E-5 | 1/℃ | ASTM E831 |
| MD：23~60℃ | 8.1E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.8E-5 | 1/℃ | ASTM E831 |
| TD：23~60℃ | 8.6E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 to 1.0E+4 | ohms·cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 105 to 110 | °C | |
| Drying time | 8.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Barrel 1 zone temperature | 245 to 260 | °C | |
| Barrel 2 zone temperature | 245 to 260 | °C | |
| Barrel 3 zone temperature | 245 to 260 | °C | |
| Barrel 4 zone temperature | 245 to 260 | °C | |
| Connector temperature | 245 to 260 | °C | |
| Melt temperature | 245 to 260 | °C | |
| Nozzle temperature | 245 to 260 | °C | |
| Calibration temperature, first time | 35 to 75 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |