| 10% Glass Reinforced PPE+PA Alloy.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.60 to 0.80 | % | Internal Method |
| TD：3.2 mm | 0.65 to 0.85 | % | Internal Method |
| Water absorption rate | ASTM D570 | ||
| 24hr，50% RH | 0.50 | % | ASTM D570 |
| Balance, 50% RH | 1.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 53 | J/m | ASTM D256 |
| 23℃ | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 245 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 210 | ℃ | ASTM D648 |
| Vicat Softening Temp | 241 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| MD：-20~150℃ | 4.0E-5 to 5.0E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 89.6 | MPa | ASTM D638 |
| fracture | 88.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3960 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 155 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended injection volume | Nominal value | Unit | Test method |
| Drying temperature | 93 to 107 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 266 to 304 | °C | |
| Barrel middle temperature | 271 to 304 | °C | |
| Barrel front temperature | 277 to 304 | °C | |
| Nozzle temperature | 282 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 77 to 121 | °C | |
| Back pressure | 0.345 to 1.38 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.013 to 0.038 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 0.20 in/min |
| 4. 0.10 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Tungsten Electrode |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |