| About |
|---|
| Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | Good Dimensional Stability,Solvent resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D792 | ||
| — | 1.10 | g/cm³ | ASTM D792 |
| — | 1.11 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：130℃，1 hrs | 1.6 to 1.8 | % | ASTM D955 |
| MD：3.2 mm | 1.1 to 1.3 | % | Internal Method |
| TD：3.2 mm | 1.0 to 1.2 | % | Internal Method |
| Water absorption rate | ASTM D570 | ||
| 24hr，50% RH | 0.50 | % | ASTM D570 |
| Balance, 50% RH | 1.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 130 | J/m | ASTM D256 |
| 23℃ | 240 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Energy at Peak Load | 39.5 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 50.8 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 193 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 143 | ℃ | ASTM D648 |
| Vicat Softening Temp | 232 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~95℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| MD：60~138℃ | 1.3E-4 | 1/℃ | ASTM E831 |
| TD：-40~95℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| TD：60~138℃ | 1.3E-4 | 1/℃ | ASTM E831 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 116 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 59.3 | MPa | ASTM D638 |
| fracture | 55.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2250 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 95.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93 to 107 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 5. Tungsten Electrode |
| 6. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |