A new high flow GTX designed for under-the-hood applications such as power distribution boxes, relay boxes and junction boxes. Developmental name EXNX0151.&& |
Product Description | |
---|---|
Supplier | SABIC |
Generic | PPO(PPE)+PS+PA |
Material Status | Commercial: Negative |
Features | High liquidity |
Availabilitys | Asia Pacific |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.10 | g/cm³ | ASTM D792 |
Melt Flow Rate | ASTM D1238 | ||
280℃,2.16kg | 26 | g/10min | ASTM D1238 |
280℃,5.0kg | 67 | g/10min | ASTM D1238 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
yield | 65.0 | MPa | ASTM D638 |
Tensile strain | |||
fracture | 66 | % | ASTM D638 |
bending strength | |||
Fracture, 100 mm span | 93.0 | MPa | ASTM D790 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | ASTM D256 | ||
-30℃ | 93 | J/m | ASTM D256 |
23℃ | 240 | J/m | ASTM D256 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
0.45 MPa, unannealed, 6.4 mm | 195 | ℃ | ASTM D648 |
Linear coefficient of thermal expansion | ASTM E831 | ||
MD:-40~40℃ | 9.0E-5 | 1/℃ | ASTM E831 |
TD:-40~40℃ | 8.5E-5 | 1/℃ | ASTM E831 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Dielectric strength | |||
1.6 mm in oil | 22 | kV/mm | ASTM D149 |
Dissipation factor | |||
1 MHz | 0.017 | ASTM D150 |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 100 to 120 | °C | |
Drying time | 2.0 to 3.0 | hr | |
Recommended maximum moisture content | 0.070 | % | |
Hopper temperature | 60 to 80 | °C | |
Barrel rear temperature | 260 to 280 | °C | |
Barrel middle temperature | 270 to 290 | °C | |
Barrel front temperature | 280 to 300 | °C | |
Nozzle temperature | 270 to 300 | °C | |
Processing (melt) temperature | 280 to 310 | °C | |
Mold temperature | 80 to 120 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. Type I, 2.0 in/min |
3. 0.10 in/min |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |