| About |
|---|
| NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Features | High impact resistance,Conductive,Sprayable,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.4~1.7 | % | |
| TD：3.2 mm | 1.2~1.5 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 4.2 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2/50 |
| fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 30 | % | ISO 527-2/50 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| Instrument impact energy (23 ℃) | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 195 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm | 190 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B120 | 200 | ℃ | ISO 306 |
| B50 | 195 | ℃ | ISO 306 |
| Ball pressure test | |||
| 123~127℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~60℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3~1.0E+4 | ohms·cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100~120 | °C | |
| Drying time | 2.0~3.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Hopper temperature | 60~80 | °C | |
| Barrel rear temperature | 260~280 | °C | |
| Barrel middle temperature | 280 ~ 300 | °C | |
| Barrel front temperature | 290 ~320 | °C | |
| Nozzle temperature | 280 ~ 310 | °C | |
| Processing (melt) temperature | 290~320 | °C | |
| Mold temperature | 80 ~120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |