| PPE+PS GF+MF 30% filled, FR V-1, high flow&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.25 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 58 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 125 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 2.4E-5 to 3.4E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 88 | ASTM D785 | |
| tensile strength | |||
| yield | 116 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 4.0 to 6.0 | % | Internal Method |
| Bending modulus | 7940 | MPa | ASTM D790 |
| bending strength | 147 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |