| About |
|---|
| NORYL LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for light weight parts. NORYL LS6010 is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and strong flame, smoke and toxicity performance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Flame Characteristics,Low toxicity,Low density |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 5.7 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 5.70 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.20 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2220 | MPa | ASTM D638 |
| Tensile modulus | 2440 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 58.0 | MPa | ISO 527-2/50 |
| fracture | 53.0 | MPa | ASTM D638 |
| yield | 64.0 | MPa | ASTM D638 |
| yield | 64.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 20 | % | ASTM D638 |
| fracture | 8.3 | % | ISO 527-2/50 |
| yield | 4.7 | % | ISO 527-2/50 |
| yield | 4.6 | % | ASTM D638 |
| Bending modulus | 2360 | MPa | ISO 178 |
| 50 mm span | 2390 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 180 | J/m | ASTM D256 |
| 23℃ | 300 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 15 | kJ/m² | ISO 180-1A |
| 23℃ | 19 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 52.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 124 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 122 | ℃ | ASTM D648 |
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306 |
| B120 | 146 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Draeger Tube Toxicity | ASTM E662 | ||
| Flaming：1.52 mm | Pass | ASTM E662 | |
| Non-Flaming：1.52 mm | Pass | ASTM E662 | |
| Flame Spread Index（1.52 mm） | 15.0 | ASTM E162 | |
| NBS smoke density | ASTM E662 | ||
| Flaming，4 min：1.52 mm | 30.0 | ASTM E662 | |
| Non-Flaming，4 min：1.52 mm | 7.00 | ASTM E662 | |
| Vertical combustion test | FAR 25.853 | ||
| Test a（60 s，1.52 mm），passes at | 0.0 | hr | FAR 25.853 |
| Test b（12 s，1.52 mm），passes at | 4.00 | sec | FAR 25.853 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. 4 min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |