| About |
|---|
| NORYL™ Resin LTA6020 – Asia is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | V-1,V-0,5VA |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 4.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | ISO 1133 | ||
| 280℃，5 kg | 8.00 | cm³/10min | |
| 300℃，5 kg | 20.0 | cm³/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2680 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 72.0 | MPa | ASTM D638 |
| yield | 71.0 | MPa | ISO 527-2/50 |
| fracture | 57.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 8.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 100 mm span | 2580 | MPa | ASTM D790 |
| — | 2600 | MPa | ISO 178 |
| bending strength | |||
| — | 105 | MPa | ISO 178 |
| Yield, 100 mm span | 105 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 220 | J/m | ASTM D256 |
| -40℃ | 8.0 | kJ/m² | ISO 180-1A |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| -20℃ | 10 | kJ/m² | ISO 180-1A |
| -10℃ | 11 | kJ/m² | ISO 180-1A |
| 0℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 136 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.4 mm | 126 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 123 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 155 | ℃ | ISO 306/A120 |
| B120 | 144 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：-40~40℃ | 8.0E-5 | 1/℃ | |
| TD：-40~40℃ | 8.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA | ||
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 825 | ℃ | |
| 1.5 mm | 825 | ℃ | |
| 2 mm | 825 | ℃ | |
| 3 mm | 825 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80.0 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 4. 0.079 in/min |
| 5. at Yield |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |