NORYL™ N1050 resin

About
Noryl* N1050 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a UL94 V0 rating at 1.5 mm and 5VA at 2.5 mm with a specific density of 1.11 g/cm^3. Noryl N1050 may be an excellent material candidate for application requiring electrically insulating properties, low moisture absorption and low warpage.

About

Noryl* N1050 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a UL94 V0 rating at 1.5 mm and 5VA at 2.5 mm with a specific density of 1.11 g/cm^3. Noryl N1050 may be an excellent material candidate for application requiring electrically insulating properties, low moisture absorption and low warpage.

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS
Material Status	Commercial: Active
Features	Insulation
Availabilitys	North America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ASTM D792
Melt Flow Rate
250℃，10.0kg	17	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.50 to 0.70	%	ASTM D570
Water absorption rate
23℃，24hr	0.060	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 23 ℃	63	MPa	ASTM D638
Tensile strain
fracture	40	%	ASTM D638
bending strength	98	MPa	ASTM D790
Bending modulus	2530	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	105	℃	ASTM D648
Linear coefficient of thermal expansion
MD	7.0E-5	1/℃	ASTM E831

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
1.50 mm	V-0	UL 94
2.00 mm	5VB	UL 94
2.50 mm	5VA	UL 94

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	117	J/m	ASTM D256

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80-120	°C
Drying time	2 to6	hr
Recommended maximum moisture content	0.020	%
Barrel rear temperature	260 to 290	°C
Barrel middle temperature	270 to 300	°C
Barrel front temperature	280 to 310	°C
Nozzle temperature	290 to 320	°C
Mold temperature	60 to 130	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.