| About |
|---|
| NORYL™ Resin N110HG是一种非填充材料。根据ISO306标准，在116℃时的微卡软化点为B/120。. NORYL N110HG可应用于需要高光泽度的产品中。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Flame Characteristics,Good wear resistance,Heat Resistance, Good |
| Availabilitys | Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, 50 mm/min | 45 | MPa | ISO 527 |
| tensile strength | |||
| 50 mm/min | 40 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile strain | |||
| 50 mm/min | 30 | % | ISO 527 |
| Tensile modulus | |||
| 1 mm/min | 2200 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 60 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 200 | MPa | ISO 178 |
| Hardness H358/30 | 95 | MPa | ISO 2039-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*4 | 11 | kJ/m² | ISO 180-1A |
| Impact strength of cantilever beam notch | |||
| -30℃，80*10*4 | 5 | kJ/m² | ISO 180-1A |
| Charpy Notched Impact Strength | |||
| 23 ℃, 80 * 10 * 3, 62mm span | 11 | kJ/m² | ISO 179/1eA |
| -30 ℃, 80 * 10 * 4, 62mm span | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity | 0.22 | W/m-℃ | ISO 8302 |
| Linear coefficient of thermal expansion | |||
| 23 ℃ to 80 ℃, flowing | 7.E-05 | 1/℃ | ISO 11359-2 |
| 23 ℃ to 80 ℃, horizontal | 9.E-05 | 1/℃ | ISO 11359-2 |
| Ball pressure test | |||
| 75℃±2℃ | PASSES | IEC 60695-10-2 | |
| Vicat Softening Temp | |||
| B50 | 115 | ℃ | ISO 306 |
| B120 | 115 | ℃ | ISO 306 |
| A50 | 120 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8 MPa, 100 mm span | 95 | ℃ | ISO 75/Ae |
| 0.45 MPa, 100 mm span | 105 | ℃ | ISO 75/Be |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Stretching rod shrinkage mold | 0.5-0.7 | % | SABIC Method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.2 | % | ISO 62 |
| 23℃，50% RH | 0.07 | % | ISO 62 |
| Melt Volume Rate | |||
| 280℃，3.8 kg | 15 | cm³/10min | ISO 1133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | >1.0E+15 | IEC 60093 | |
| Dielectric strength | |||
| 3.2 mm in oil | 19 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50-60 Hz | 2.6 | IEC 60250 | |
| 1 MHz | 2.6 | IEC 60250 | |
| Dissipation factor | |||
| 50-60 Hz | 0.004 | IEC 60250 | |
| 1 MHz | 0.001 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant grade 94HB | 1.5 | mm | UL 94 |
| Level 2 flame retardant rating 94HB | 3 | mm | UL 94 |
| Glowing wire flammability index | |||
| 960 ℃ | 3.2 | mm | IEC 60695-2-12 |
| Extreme oxygen index | |||
| LOI | 19 | % | ISO 4589 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 80-100 | ℃ | |
| Drying time | 2-4 | hrs | |
| Melt temperature | 280-300 | ℃ | |
| Nozzle temperature | 260-280 | ℃ | |
| Front temperature | 280-300 | ℃ | |
| Mid section temperature | 260-280 | ℃ | |
| Post stage temperature | 240-260 | ℃ | |
| Hopper temperature | 60-80 | ℃ | |
| Mold temperature | 60-100 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |