NORYL™ N1250 resin

About
NORYL N1250是一种未填充的，注塑成型的改性聚苯醚树脂。该树脂具有良好的尺寸稳定性和良好的流动性，还使用非氯化的非溴化FR添加剂，在0.75mm下达到得V0 UL94等级，在2.5mm下达到V0-5VA等级，特定密度为1.11g / cm 3。NORYL N1250具有137摄氏度的耐热维持电阻，是应用在电气绝缘方面的优异材料。

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS
Material Status	Commercial: Negative
Features	Good Dimensional Stability,Good liquidity
Availabilitys	Africa & Middle East ,North America,Latin America,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, Type I, 50 mm/min	63	MPa	ASTM D638
Fracture, 50 mm/min	55	MPa	ISO 527
Yield, 50 mm/min	75	MPa	ISO 527
yield	69	MPa	Internal Method
Model I, 50 mm/min	80	MPa	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	15	%	ASTM D638
Fracture, 50 mm/min	8	%	ISO 527
fracture	45	%	Internal Method
Yield, 50 mm/min	4.5	%	ISO 527
Type I, 50 mm/min	5	%	ASTM D638
bending strength	1100	kgf/cm²	ASTM D 790
Yield, 2 mm/min	109	MPa	ISO 178
Yield, 1.30 mm/min, 50 mm span	121.644	MPa	ASTM D790
Bending modulus	25900	kgf/cm²	ASTM D 790
2 mm/mim	2530	MPa	ISO 178
1.3 mm / min，50mm跨距	2992.05	MPa	ASTM D790
Tensile modulus
50 mm/min	2717.37	MPa	ASTM D638
1 mm/min	2620	MPa	ISO 527

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	88.2	J/m	ASTM D256
23℃，80103	8	kJ/m²	ISO 180-1A
-30℃，80103	6	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 4, 62mm span	7	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, 64 mm span	119	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	125	℃	ASTM D648
0.45 MPa, unannealed, 3.2 mm	136	℃	ASTM D648
Linear coefficient of thermal expansion
MD：-40~40℃	6.12E-05	1/℃	ASTM E831
MD：-40~40℃	6.84E-05	1/℃	ASTM E831
Linear coefficient of thermal expansion
TD：-30~40℃	6.8E-05	1/℃	ISO 11359-2
Ball pressure test
125℃±2℃	通过		IEC 60695-10-2
Vicat Softening Temp	139	℃	ISO 306
Relative temperature index
Non mechanical impact performance	110	℃	UL 746B
Electrical performance	110	℃	UL 746B
Impact mechanical performance	105	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Density	1.1		ASTM D792
Water absorption for 24 hours	0.07	%	ASTM D 570
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
MD：24 hrs	0.5	%	ISO 294
Density	1.1	g/cm³	ISO 1183
Water absorption rate
23℃，50% RH	0.05	%	ISO 62
Saturation, 23 ℃	0.25	%	ISO 62
Melt Volume Rate
280℃，5 kg	12	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Hot wire ignition {PLC)	0	PLC Code	UL 746A
High voltage arc marking rate {PLC}	4	PLC Code	UL 746A
High current arc ignition (surface {PLC})	0	PLC Code	UL 746A
Dielectric strength
3.2 mm in oil	49	kV/mm	IEC 60243-1
Compared to the leakage tracing index	250	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
0.40 mm	V-2	UL 94
0.75 mm	V-0	UL 94
2.50 mm	5VA	UL 94

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	105 – 110	°C
Drying time	3 – 4	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.02	%
Melt temperature	275 – 305	°C
Nozzle temperature	275 – 305	°C
Temperature in the first three zones	265 – 305	°C
Middle Zone 2 Temperature	255 – 300	°C
Rear – Zone 1 Temperature	245 – 295	°C
Mold temperature	70 – 100	°C
Back pressure	0.3 – 0.7	MPa
Screw speed	20 – 100	rpm
Shoot to cylinder size	30 – 70	%
Depth of exhaust groove	0.038 – 0.051	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.