| NORYL? NH4050 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for light-weight parts. This injection-molding resin is available in custom colors. NORYL? NH4050 resin may be an excellent candidate for industrial battery applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Hydrolysis stability,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 25 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 32.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2680 | MPa | ASTM D638 |
| Tensile modulus | 2640 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 51.0 | MPa | ISO 527-2/50 |
| fracture | 52.0 | MPa | ASTM D638 |
| yield | 67.0 | MPa | ISO 527-2/50 |
| yield | 67.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 19 | % | ASTM D638 |
| fracture | 10 | % | ISO 527-2/50 |
| yield | 4.4 | % | ASTM D638 |
| yield | 4.3 | % | ISO 527-2/50 |
| Bending modulus | 2570 | MPa | ISO 178 |
| 50 mm span | 2830 | MPa | ASTM D790 |
| bending strength | 108 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 108 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 160 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 48.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 101 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 94.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 118 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 120 | ℃ | ISO 306 |
| B120 | 120 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 8.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 8.2E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93 to 99 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 227 to 277 | °C | |
| Barrel middle temperature | 238 to 282 | °C | |
| Barrel front temperature | 249 to 288 | °C | |
| Nozzle temperature | 260 to 288 | °C | |
| Processing (melt) temperature | 260 to 288 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |