| About |
|---|
| NORYL NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm and is also non-halogenated according to VDE/DIN 472 part 815. NORYL NH6020 resin has a HDT > of 120 deg C, pass the BPT @ 125 deg C, pass the GWIT 775 deg C @ 1, 2 and 3 mm, has the CTI value > 250 V and may be an excellent material candidate for unattended appliances components, where IEC 60335 applies.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 14 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 11.6 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.18 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2740 | MPa | ASTM D638 |
| — | 2740 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 78.9 | MPa | ASTM D638 |
| yield | 77.4 | MPa | ISO 527-2/50 |
| fracture | 67.6 | MPa | ASTM D638 |
| fracture | 56.6 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.6 | % | ASTM D638 |
| yield | 4.6 | % | ISO 527-2/50 |
| fracture | 6.1 | % | ASTM D638 |
| fracture | 4.2 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 3020 | MPa | ASTM D790 |
| — | 2690 | MPa | ISO 178 |
| bending strength | |||
| — | 114 | MPa | ISO 178 |
| Yield, 50 mm span | 121 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.8 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 36 | J/m | ASTM D256 |
| 23℃ | 49 | J/m | ASTM D256 |
| -30℃ | 5.4 | kJ/m² | ISO 180-1A |
| 23℃ | 8.1 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 18.4 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 125 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 125 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 150 | ℃ | ASTM D1525 11 |
| B50 | 141 | ℃ | ISO 306 |
| B120 | 151 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.8E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-6 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 7.8E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 110 | ℃ | UL 746 |
| Electrical performance | 110 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.5E+16 to 4.2E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm in oil | 27 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 2.9E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| 2 mm | 800 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 37 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 80 to 100 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 300 to 320 | °C | |
| Mold temperature | 100 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |