| About |
|---|
| Noryl* NH7010HF resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts. The resin will be available in custom colors and is suitable for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-0,5VA |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.25 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2180 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 59.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 5.0 | % | ASTM D638 |
| fracture | 12 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2460 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 69 | J/m | ASTM D256 |
| 23℃ | 230 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 53.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 138 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 139 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 159 | ℃ | ASTM D1525 6 |
| B120 | 162 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 145℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ASTM E831 , ISO 11359-2 | ||
| MD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| Relative temperature index | 105 | ℃ | UL 746 |
| Electrical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 266 to 316 | °C | |
| Barrel middle temperature | 277 to 321 | °C | |
| Barrel front temperature | 288 to 327 | °C | |
| Nozzle temperature | 299 to 327 | °C | |
| Processing (melt) temperature | 299 to 327 | °C | |
| Mold temperature | 82 to 110 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4 mm |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. Approximate Maximum |
| 8. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |