| NORYL™ Resin NHP5054 – Asia is a Polyphenylene Ether (PPE) product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Automotive. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 24 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 120 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 6000 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 150 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 120 | ℃ | ASTM D648 |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 0.10 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |