| About |
|---|
| NORYL NHP9023 resin is 15% glass fiber reinforced, with a non-halogen flame retardant (UL94 V-0 at 1.5 mm) and high heat distortion temperature (150 C)&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-1,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.20 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 61 | J/m | ASTM D256 |
| 23℃ | 72 | J/m | ASTM D256 |
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 500 | J/m | ASTM D4812 |
| 23℃ | 500 | J/m | ASTM D4812 |
| -30℃ | 28 | kJ/m² | ISO 180/1U |
| 23℃ | 27 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 10.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 153 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 154 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 155 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 161 | ℃ | ISO 306 |
| B120 | 163 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831 , ISO 11359-2 | ||
| MD：23~80℃ | 3.5E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| TD：23~80℃ | 6.4E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| Relative temperature index | 65.0 | ℃ | UL 746 |
| Electrical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 | |
| Tensile modulus | |||
| — | 5400 | MPa | ASTM D638 |
| — | 5600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 112 | MPa | ASTM D638 |
| fracture | 112 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.9 | % | ASTM D638 |
| fracture | 2.7 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 5200 | MPa | ASTM D790 |
| — | 5200 | MPa | ISO 178 |
| bending strength | |||
| — | 163 | MPa | ISO 178 |
| Yield, 50 mm span | 163 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 266 to 316 | °C | |
| Barrel middle temperature | 277 to 321 | °C | |
| Barrel front temperature | 288 to 327 | °C | |
| Nozzle temperature | 299 to 327 | °C | |
| Processing (melt) temperature | 299 to 327 | °C | |
| Mold temperature | 82 to 110 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |