| About |
|---|
| PPE+PP blend. High Impact, Good Heat Resistance&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.80 to 1.2 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1340 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 35.9 | MPa | |
| fracture | 32.4 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 6.5 | % | |
| fracture | 200 | % | |
| Bending modulus | |||
| 50 mm span | 1550 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 51.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 150 | J/m | |
| 23℃ | 440 | J/m | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 27.8 | J | |
| 23℃，Total Energy | 38.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 113 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 77.2 | ℃ | |
| Vicat Softening Temp | 139 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 8.1E-5 | 1/℃ | |
| TD：-40~40℃ | 1.1E-4 | 1/℃ | |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.52 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60.0 to 65.6 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 227 to 277 | °C | |
| Barrel middle temperature | 238 to 282 | °C | |
| Barrel front temperature | 249 to 288 | °C | |
| Nozzle temperature | 260 to 288 | °C | |
| Processing (melt) temperature | 260 to 288 | °C | |
| Mold temperature | 32.2 to 48.9 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Drying temperature | 60.0 to 65.6 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 143 to 154 | °C | |
| Barrel 2 zone temperature | 254 to 266 | °C | |
| Barrel 3 zone temperature | 271 to 282 | °C | |
| Barrel 4 zone temperature | 271 to 282 | °C | |
| Connector temperature | 263 to 268 | °C | |
| Melt temperature | 271 to 279 | °C | |
| Nozzle temperature | 263 to 268 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |