NORYL PPX™ PPX7200 resin

About
NORYL PPX™ PPX7200 resin PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.&&

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS+PP
Material Status	Commercial: Active
Features	Good surface appearance,Solvent resistance
Availabilitys	North America,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.988	g/cm³	ASTM D792
Density	0.990	g/cm³	ISO 1183
Melt Flow Rate
260℃，5.0kg	16	g/10min	ASTM D1238
Melt Volume Rate
260℃，5 kg	18.0	cm³/10min	ISO 1133
Shrinkage rate
TD：3.2 mm	0.60 to 0.80	%	Internal Method
MD：3.2 mm	0.60 to 0.80	%	Internal Method
Water absorption rate
Saturation, 23 ℃	0.050	%	ISO 62
Equilibrium, 23 ℃, 50% RH	0.020	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1240	MPa	ASTM D638
Tensile modulus	1670	MPa	ISO 527-1-2
tensile strength
fracture	27.6	MPa	ASTM D638
fracture	28.0	MPa	ISO 527-2/50
yield	33.8	MPa	ASTM D638
yield	34.0	MPa	ISO 527-2/50
Tensile strain
fracture	130	%	ASTM D638
fracture	120	%	ISO 527-2/50
yield	10	%	ASTM D638
yield	8.2	%	ISO 527-2/50
Bending modulus	1610	MPa	ISO 178
50 mm span	1450	MPa	ASTM D790
bending strength	48.0	MPa	ISO 178
bending strength
Yield, 50 mm span	49.0	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	6.1	kJ/m²	ISO 179/1eA
23℃	12	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	80	kJ/m²	ISO 179/1eU
23℃	No Break		ISO 179/1eU
Impact strength of cantilever beam notch			ASTM D256
-30℃	0.85	J/m	ASTM D256
23℃	150	J/m	ASTM D256
Impact strength of cantilever beam notch			ISO 180/1A
23℃	1400	J/m	ASTM D4812
-30℃	8.0	kJ/m²	ISO 180-1A
23℃	14	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	No Break		ISO 180/1U
23℃	No Break		ISO 180/1U
Dart impact equipped with measuring instruments
23℃，Total Energy	36.2	J	ASTM D3763

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	73.4	℃	ISO 75-2/Af
1.8 MPa, unannealed, 3.2 mm	71.1	℃	ASTM D648
0.45 MPa, unannealed, 3.2 mm	110	℃	ASTM D648
Vicat Softening Temp	146	℃	ASTM D1525 10
Vicat Softening Temp
B50	103	℃	ISO 306
B120	107	℃	ISO 306/B120
Linear coefficient of thermal expansion
TD：-40~40℃	1.1E-4	1/℃	ASTM E831
TD：-40~40℃	1.1E-4	1/℃	ISO 11359-2
MD：-40~40℃	9.9E-5	1/℃	ISO 11359-2
MD：-40~40℃	9.9E-5	1/℃	ASTM E831

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	60 to 66	°C
Drying time	2.0 to 4.0	hr
Drying time, maximum	8.0	hr
Recommended maximum moisture content	0.020	%
Recommended injection volume	30 to 70	%
Barrel rear temperature	227 to 277	°C
Barrel middle temperature	238 to 282	°C
Barrel front temperature	249 to 288	°C
Nozzle temperature	260 to 288	°C
Processing (melt) temperature	260 to 288	°C
Mold temperature	32 to 49	°C
Back pressure	0.345 to 0.689	MPa
Screw speed	20 to 100	rpm
Vent depth	0.038 to 0.051	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.