| About |
|---|
| NORYL PPX™ PPX830 resin NORYL PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. NORYL PPX830 is an opaque material available in limited colors only.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Solvent resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 6.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| MD：3.2 mm | 0.20 to 0.25 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7600 | MPa | ASTM D638 |
| Tensile modulus | 7700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 101 | MPa | ASTM D638 |
| fracture | 98.0 | MPa | ISO 527-2/5 |
| yield | 101 | MPa | ASTM D638 |
| yield | 98.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 3.2 | % | ISO 527-2/5 |
| fracture | 100 | % | ASTM D638 |
| yield | 3.2 | % | ISO 527-2/5 |
| yield | 2.9 | % | ASTM D638 |
| Bending modulus | 7100 | MPa | ISO 178 |
| 50 mm span | 6600 | MPa | ASTM D790 |
| bending strength | 141 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 144 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 36 | kJ/m² | ISO 179/1eU |
| 23℃ | 39 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 650 | J/m | ASTM D4812 |
| 23℃ | 95 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 42 | kJ/m² | ISO 180/1U |
| 23℃ | 42 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 10.0 | J | ASTM D3763 |
| 23℃，Total Energy | 15.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 153 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 156 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 168 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 166 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B120 | 150 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~95℃ | 1.3E-4 | 1/℃ | ASTM E831 |
| TD：-30~80℃ | 1.2E-4 | 1/℃ | ISO 11359-2 |
| MD：-40~95℃ | 2.5E-5 | 1/℃ | ASTM E831 |
| MD：-30~80℃ | 2.5E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 65 to 75 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 245 to 290 | °C | |
| Barrel middle temperature | 250 to 290 | °C | |
| Barrel front temperature | 255 to 290 | °C | |
| Nozzle temperature | 260 to 300 | °C | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 40 to 65 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |