| About |
|---|
| PPE+PP blend. Suitable for painted exterior automotive applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | Sprayable |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.988 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.70 | % | |
| TD：3.2 mm | 0.60 to 0.80 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1170 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 34.0 | MPa | |
| fracture | 33.0 | MPa | |
| Tensile strain | |||
| yield | 8.0 | % | |
| fracture | 120 | % | |
| Bending modulus | |||
| 50 mm span | 1340 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 49.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 590 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 37.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 112 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 85.0 | ℃ | |
| Vicat Softening Temp | 85.0 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.6E-4 | 1/℃ | |
| TD：-40~40℃ | 7.2E-5 | 1/℃ | |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Squeeze description | Nominal value | Unit | Test method |
| Drying temperature | 60 to 65 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 225 to 275 | °C | |
| Barrel middle temperature | 240 to 280 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |