| About |
|---|
| High modulus/impact/heat PPE+PP&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.988 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 14 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.70 | % | |
| TD：3.2 mm | 0.60 to 0.80 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1240 | MPa | ASTM D638 |
| — | 1370 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 35.0 | MPa | ASTM D638 |
| yield | 35.0 | MPa | ISO 527-2/50 |
| fracture | 34.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 8.0 | % | ASTM D638 |
| fracture | 130 | % | ASTM D638 |
| fracture | 75 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 1370 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 51.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 530 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| -30℃，Total Energy | 30.0 | J | |
| 23℃，Total Energy | 37.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 112 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 85.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 86.0 | ℃ | ASTM D1525 6 |
| A50 | 131 | ℃ | ISO 306/A50 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.6E-4 | 1/℃ | |
| TD：-40~40℃ | 9.7E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 65 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 225 to 275 | °C | |
| Barrel middle temperature | 240 to 280 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |