| PP+PPE+PS. UV-stabilized. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61/UL94 listings pending.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 0.988 | g/cm³ | ASTM D792 |
| — | 0.990 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 16 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.060 to 0.080 | % | |
| MD：3.2 mm | 0.60 to 0.80 | % | |
| TD：3.2 mm | 0.60 to 0.80 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1240 | MPa | ASTM D638 |
| — | 1670 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 33.0 | MPa | ASTM D638 |
| yield | 34.0 | MPa | ISO 527-2/50 |
| fracture | 27.0 | MPa | ASTM D638 |
| fracture | 28.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ASTM D638 |
| yield | 8.2 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 1440 | MPa | ASTM D790 |
| — | 1600 | MPa | ISO 178 |
| bending strength | |||
| — | 48.0 | MPa | ISO 178 |
| Yield, 50 mm span | 48.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 12 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 80 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 150 | J/m | ASTM D256 |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1400 | J/m | ASTM D4812 |
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 36.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 110 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 71.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 146 | ℃ | ASTM D1525 11 |
| B50 | 103 | ℃ | ISO 306 |
| B120 | 107 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 9.9E-5 | 1/℃ | |
| TD：-40~40℃ | 1.1E-4 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 65 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 225 to 275 | °C | |
| Barrel middle temperature | 240 to 280 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |