| About |
|---|
| Unfilled, non-FR. Higher heat resistance than N110 (BOZ) and px0844 (USA). For automotive interiors. 250F (121C) DTUL.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，2.16 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 130 | J/m | ASTM D256 |
| 23℃ | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 128 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 129 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：0~100℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 58.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 30 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2360 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 93.1 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 249 to 299 | °C | |
| Barrel middle temperature | 260 to 304 | °C | |
| Barrel front temperature | 271 to 310 | °C | |
| Nozzle temperature | 282 to 310 | °C | |
| Processing (melt) temperature | 282 to 310 | °C | |
| Mold temperature | 77 to 104 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |