| PPE+PS blend. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Insulation |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 37 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 – 0.70 | % | Internal Method |
| TD | 0.50 – 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 55 | MPa | ASTM D638 |
| fracture | 41 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 3.1 | % | ASTM D638 |
| fracture | 17 | % | ASTM D638 |
| Tensile modulus | 2400 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 79 | MPa | ASTM D638 |
| Yield, 1.30 mm/min, 50 mm span | 80 | MPa | ASTM D638 |
| Bending modulus | |||
| 2.60 mm/min, 100 mm span | 2200 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 1174 | j/m | ASTM D4812 |
| 23℃ | 300 | j/m | ASTM D256 |
| -30℃ | 90 | j/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 84 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 72 | ℃ | ASTM D648 |
| Vicat Softening Temp | 107 | ℃ | ASTM D1525 |
| Relative temperature index | 95 | ℃ | UL 746 |
| Electrical performance | 95 | ℃ | UL 746 |
| Impact mechanical performance | 80 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.3E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in air | 17.7 | kV/mm | ASTM D149 |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Glowing wire flammability index | |||
| 1.5 mm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.01 mm | HB | UL 94 | |
| 1.47 mm | V-0 | UL 94 | |
| 2.99 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended injection volume | Nominal value | Unit | Test method |
| Drying temperature | 75 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 250-275 | °C | |
| Barrel middle temperature | 240-275 | °C | |
| Barrel front temperature | 215-265 | °C | |
| Nozzle temperature | 250-275 | °C | |
| Processing (melt) temperature | 277 to 304 | °C | |
| Mold temperature | 55-75 | °C | |
| Back pressure | 0.3-0.7 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |