| About |
|---|
| PPE + PS混合物。无填充。 UL94 HB额定值。 吸水率低。 水解稳定性。 尺寸稳定性。 适用于流体工程应用：阀门组件，水泵外壳等。此等级将不再支持生物相容性信息，不应用于需要生物相容性的医疗应用。 替代等级HN731A。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 12 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5~0.8 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.13 | % | ISO 62-1 |
| Equilibrium, 23 ℃, 50% RH | 0.04 | % | ISO 62-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 40 | MPa | ISO 527-2/5 |
| fracture | 40 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 70 | % | ISO 527-2/5 |
| fracture | 70 | % | ISO 527-2/5 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | |||
| yield | 80 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | kJ/m² | ISO 180-1U |
| -30℃ | 55 | kJ/m² | ISO 180-1U |
| Charpy Notched Impact Strength | |||
| 23℃ | 23 | kJ/m² | ISO 179/1eA |
| Dart impact equipped with measuring instruments (23 ℃) | 55 | J | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 124 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 133 | ℃ | ASTM D1525 12 |
| B120 | 135 | ℃ | ASTM D1525 12 |
| Ball pressure test | |||
| 123~127℃ | 通过 | ||
| 125℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.3E-05 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 8.3E-05 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 105~110 | °C | |
| Drying time | 3~4 | hrs | |
| Accumulated drying time | 8 | hrs | |
| Maximum moisture content | 0.02 | % | |
| Temperature at the rear of the barrel | 250~300 | °C | |
| Temperature in the middle of the barrel | 260~305 | °C | |
| Front temperature of material barrel | 270~310 | °C | |
| Nozzle temperature | 280~310 | °C | |
| Melt Temperature | 280~310 | °C | |
| Mold temperature | 70~105 | °C | |
| Back pressure | 0.3~0.7 | MPa | |
| Screw speed | 20~100 | rpm | |
| Shoot to cylinder size | 30~70 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |