| About |
|---|
| Extrusion grade. Excellent impact strength. 185F (85C) DTUL. UL94 V-1 rated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.070 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 160 | J/m | |
| 23℃ | 390 | J/m | |
| Drop hammer impact | |||
| -40℃ | 13.0 | J | |
| -30℃ | 24.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 93.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 82.0 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 2.80 | ||
| 50 kHz | 2.80 | ||
| Dissipation factor | |||
| 50 Hz | 4.0E-3 | ASTM D150 | |
| 60 Hz | 4.0E-3 | ASTM D150 | |
| 1 MHz | 3.5E-3 | IEC 60250 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| Radiation Plate Listing | TRUE |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 113 | ASTM D785 | |
| tensile strength | |||
| yield | 42.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2270 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 67.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 170 | °C | |
| Barrel 2 zone temperature | 170 | °C | |
| Barrel 3 zone temperature | 190 | °C | |
| Barrel 4 zone temperature | 190 | °C | |
| Connector temperature | 205 | °C | |
| Melt temperature | 195 to 210 | °C | |
| Nozzle temperature | 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 4. Tungsten Electrode |
| 5. Surface |
| 6. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |