| About |
|---|
| Improved reliability and productivity. Thin wall capability. UL94 V-0/5VA rated. All data at 20% weight reduction and 0.250″ wall.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Foaming performance |
| Availabilitys | North America |
| Process Methods | Foam treatment |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：6.4 mm | 0.60 to 0.80 | % | |
| TD：6.4 mm | 0.60 to 0.80 | % | |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，6.4 mm | 340 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 89.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 73.0 | ℃ | |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 3 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 4.00 mm | UL 94 | ||
| Flame Class Minimum Density（Foam） | 900 | kg/m³ | |
| Radiation Plate Listing | TRUE |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Reduction | |||
| Foam – Impact：6.40 mm | 20 | % | |
| Foam – Mechanical：6.40 mm | 20 | % | |
| Foam – Physical：6.40 mm | 20 | % | |
| Foam – Thermal：6.40 mm | 20 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 | |
| tensile strength | |||
| Yield, 6.35 mm | 28.0 | MPa | |
| Fracture, 6.35 mm | 28.0 | MPa | |
| Tensile strain | |||
| Yield, 6.35 mm | 7.3 | % | |
| Fracture, 6.35 mm | 14 | % | |
| Bending modulus | |||
| 6.40 mm | 1740 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 52.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 152 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| Injection instructions | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 3. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |