| About |
|---|
| Foamable resin. All properties at 10% density reduction; 0.250″ thick test specimens.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Foaming performance |
| Availabilitys | North America |
| Process Methods | Foam treatment |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 0.998 | g/cm³ | |
| — | 1.11 | g/cm³ | |
| Shrinkage rate | |||
| MD：6.4 mm | 0.60 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| Outdoor applicability | f2 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 6.35 mm | 29.0 | MPa | |
| Fracture, 6.35 mm | 28.0 | MPa | |
| Tensile strain | |||
| Yield, 6.35 mm | 5.7 | % | |
| Fracture, 6.35 mm | 13 | % | |
| Bending modulus | |||
| 6.40 mm | 2130 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 66.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，6.4 mm | 280 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak | 57.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 89.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 78.0 | ℃ | |
| Relative temperature index | 85.0 | ℃ | UL 746 |
| Electrical performance | 85.0 | ℃ | UL 746 |
| Impact mechanical performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.00 mm | V-1 | ||
| 4.70 mm | 5VA | ||
| Flame Class Minimum Density（Foam） | 1.000 | g/cm³ | |
| Radiation Plate Listing | TRUE |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Reduction | |||
| Foam – Impact：6.40 mm | 10 | % | |
| Foam – Mechanical：6.40 mm | 10 | % | |
| Foam – Physical：6.40 mm | 10 | % | |
| Foam – Thermal：6.40 mm | 10 | % |
| Process Conditions | |||
|---|---|---|---|
| Injection instructions | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Foam Molded |
| 3. Tungsten Electrode |
| 4. Surface |
| 5. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |