| About |
|---|
| PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| 1.23 | g/cm³ | ASTM D792 | |
| 12 | g/10min | ASTM D1238 | |
| 2.00 | cm³/10min | ISO 1133 | |
| 0.20 to 0.40 | % | Internal Method | |
| 0.060 | % | ASTM D570 | |
| 0.12 | % | ISO 62 | |
| 0.040 | % | ISO 62 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 6500 | MPa | ASTM D638 | |
| 6000 | MPa | ISO 527-1-2 | |
| 88.0 | MPa | Internal Method | |
| 100 | MPa | ASTM D638 | |
| 90.0 | MPa | ISO 527-2/5 | |
| 6.0 to 8.0 | % | Internal Method | |
| 3.0 | % | ASTM D638 | |
| 3.0 | % | ISO 527-2/5 | |
| 5570 | MPa | ASTM D790 | |
| 5400 | MPa | ISO 178 | |
| 150 | MPa | ISO 178 | |
| 131 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| 8.0 | kJ/m² | ISO 179/1eA | |
| 88 | J/m | ASTM D256 | |
| 9.0 | kJ/m² | ISO 180-1A | |
| 10 | kJ/m² | ISO 180-1A | |
| 550 | J/m | ASTM D4812 | |
| 30 | kJ/m² | ISO 180/1U | |
| 20.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 137 | ℃ | ASTM D648 | |
| 138 | ℃ | ASTM D648 | |
| 135 | ℃ | ISO 75-2/Af | |
| 140 | ℃ | ISO 306 | |
| 147 | ℃ | ISO 306/B120 | |
| 2.8E-5 to 4.5E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Maximum Moisture Content | 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Rear Temperature Zone 1 | 265 to 315 | °C | |
| Middle Temperature Zone 2 | 275 to 320 | °C | |
| Front Temperature Zone 3 | 290 to 325 | °C | |
| Nozzle temperature | 300 to 325 | °C | |
| Melt Temperature | 300 to 325 | °C | |
| Mold Temperature | 80 to 110 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.39 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.10 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |