| About |
|---|
| PPE+PS blend. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant (restrictions apply). Combines good hydrolytic stability and dimensional stability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low moisture absorption,Low warping,Low contractility,Solvent resistance,Hydrolysis stability |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 9.2 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Molding shrinkage | |||
| MD：3.2 mm | 0.50 to 0.70 | % | |
| TD：3.2 mm | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24hr | 0.060 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.23 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| -40℃ | 130 | J/m | ASTM D256 |
| 23℃ | 210 | J/m | ASTM D256 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 48.0 | J | ASTM D3763 |
| Gardner Impact | |||
| -40℃ | 5.00 | J | |
| -30℃ | 25.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 137 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 117 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 126 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 115 | ℃ | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| — | 148 | ℃ | ASTM D1525 10 |
| B50 | 135 | ℃ | ISO 306 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Coeff. of linear thermal expansion | |||
| MD：-40~40℃ | 9.2E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 9.5E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | 105 | ℃ | UL 746 |
| Electrical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Strength | |||
| 3.2 mm in oil | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 60 Hz | 2.65 | ||
| 50 kHz | 2.65 | ||
| Dissipation Factor | |||
| 50 Hz | 4.0E-4 | ||
| 60 Hz | 4.0E-4 | ||
| Arc Resistance | PLC 7 | ASTM D495 | |
| Compared Tracking Index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Track Rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.50 mm | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| Tensile Modulus | |||
| — | 2860 | MPa | ASTM D638 |
| — | 2300 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| yield | 7.2 | % | ASTM D638 |
| yield | 5.0 | % | ISO 527-2/50 |
| fracture | 28 | % | ASTM D638 |
| fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50 mm span | 2640 | MPa | ASTM D790 |
| 100 mm span | 2420 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| — | 75.0 | MPa | ISO 178 |
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| Yield, 100 mm span | 89.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 105 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Maximum Moisture Content | 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Rear Temperature Zone 1 | 250 to 300 | °C | |
| Middle Temperature Zone 2 | 260 to 305 | °C | |
| Front Temperature Zone 3 | 270 to 310 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Melt Temperature | 280 to 310 | °C | |
| Mold Temperature | 75 to 105 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.10 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Tungsten Electrode |
| 12. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |