| About |
|---|
| PPE+PS blend. For medical devices and pharmaceutical applications. NORYL HN731SE is an unfilled material, with a Vicat B/120 of 135C according ISO 306. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant (restrictions apply).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Biocompatible |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Water Absorption | |||
| Saturation, 23 ℃ | 0.23 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| yield | 55.0 | MPa | |
| fracture | 50.0 | MPa | |
| Tensile Strain | |||
| yield | 5.0 | % | |
| fracture | 30 | % | |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Strength | 75.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Izod Notched Impact strength | |||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 15 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed, 100 mm span | 115 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| B50 | 135 | ℃ | ISO 306 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Coeff. of linear thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | |
| TD：23~80℃ | 7.0E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 60 to 80 | °C | |
| Rear Temperature Zone 1 | 240 to 260 | °C | |
| Middle Temperature Zone 2 | 260 to 280 | °C | |
| Front Temperature Zone 3 | 280 to 300 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Melt Temperature | 280 to 300 | °C | |
| Mold Temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 80*10*4 sp=62mm |
| 5. 80*10*4 mm |
| 6. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |