| About |
|---|
| NORYL HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in custom colors. NORYL HNA033 resin may be an excellent material candidate for applications requiring multiple sterilization cycles. NORYL HNA033 resin is biocompatible per ISO 10993 (color dependent).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Biocompatible |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 8.3 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 to 0.90 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.15 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2310 | MPa | ASTM D638 |
| — | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 71.0 | MPa | ASTM D638 |
| yield | 68.0 | MPa | ISO 527-2/50 |
| fracture | 57.0 | MPa | ASTM D638 |
| fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.3 | % | ASTM D638 |
| yield | 5.2 | % | ISO 527-2/50 |
| fracture | 30 | % | ASTM D638 |
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2460 | MPa | ASTM D790 |
| — | 2590 | MPa | ISO 178 |
| bending strength | |||
| — | 107 | MPa | ISO 178 |
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 140 | J/m | ASTM D256 |
| 23℃ | 190 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 47.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 140 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 141 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 161 | ℃ | ASTM D1525 9 |
| B50 | 160 | ℃ | ISO 306 |
| B120 | 162 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.1E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 6.9E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 6.9E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 250 to 300 | °C | |
| Barrel middle temperature | 260 to 305 | °C | |
| Barrel front temperature | 270 to 310 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 280 to 310 | °C | |
| Mold temperature | 75 to 105 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |