| About |
|---|
| NORYL N190 is an unfilled, flame retardant material with a Vicat B/120 of 105?C according ISO 306. NORYL N190 is V0 at 1.52 mm and 5VA at 3.12 mm according UL94 and halogen free according VDE/DIN 472 part 815. NORYL N190 is available in all colours.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.32 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.0 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 90.0 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 80.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 110 | ℃ | ISO 306/A50 |
| B50 | 95.0 | ℃ | ISO 306 |
| B120 | 105 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | ||
| 95℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | |
| TD：23~80℃ | 9.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.25 | W/m/K | ISO 8302 |
| Relative temperature index | 95.0 | ℃ | UL 746 |
| Electrical performance | 95.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.60 | ||
| Dissipation factor | |||
| 50 Hz | 4.0E-4 | ||
| 60 Hz | 4.0E-4 | ||
| 1 MHz | 9.0E-4 | ||
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glowing wire flammability index | |||
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 30 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 87.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 50.0 | MPa | |
| fracture | 40.0 | MPa | |
| Tensile strain | |||
| yield | 3.0 | % | |
| fracture | 20 | % | |
| Bending modulus | 2200 | MPa | ISO 178 |
| bending strength | 75.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 220 to 240 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 260 to 280 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 8. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |