| About |
|---|
| PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 7.4 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | |
| TD | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 55 | J/m | ASTM D256 |
| 23℃ | 190 | J/m | ASTM D256 |
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 54.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 155 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 156 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 140 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 145 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 140 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B50 | 162 | ℃ | ISO 306 |
| B120 | 164 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 8.0E-5 | 1/℃ | |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | |
| Relative temperature index | 105 | ℃ | UL 746 |
| Electrical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 19 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 2.68 | ||
| 50 kHz | 2.68 | ||
| 1 MHz | 2.63 | ||
| Dissipation factor | |||
| 50 Hz | 3.1E-3 | ||
| 60 Hz | 3.1E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| Tensile modulus | |||
| — | 2380 | MPa | ASTM D638 |
| — | 2220 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 74.0 | MPa | ASTM D638 |
| yield | 75.0 | MPa | ISO 527-2 |
| fracture | 73.0 | MPa | ASTM D638 |
| fracture | 66.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.3 | % | ASTM D638 |
| yield | 5.2 | % | ISO 527-2 |
| fracture | 7.6 | % | ASTM D638 |
| fracture | 13 | % | ISO 527-2 |
| Bending modulus | |||
| 50 mm span | 2650 | MPa | ASTM D790 |
| 100 mm span | 2500 | MPa | ASTM D790 |
| — | 2520 | MPa | ISO 178 |
| bending strength | |||
| — | 112 | MPa | ISO 178 |
| Yield, 50 mm span | 110 | MPa | ASTM D790 |
| Yield, 100 mm span | 110 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 265 to 315 | °C | |
| Barrel middle temperature | 275 to 320 | °C | |
| Barrel front temperature | 290 to 325 | °C | |
| Nozzle temperature | 300 to 325 | °C | |
| Processing (melt) temperature | 300 to 325 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.10 in/min |
| 6. 0.051 in/min |
| 7. 80*10*4 mm |
| 8. 120*10*4 mm |
| 9. Tungsten Electrode |
| 10. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |