| NORYL PX1860 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm with a specific density of 1.1 g/cm^3. NORYL PX1860 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 15.0 | cm³/10min | |
| 280℃，2.16 kg | 34.0 | cm³/10min | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.13 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.020 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3140 | MPa | ASTM D638 |
| — | 2510 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 52.0 | MPa | ASTM D638 |
| yield | 61.0 | MPa | ISO 527-2/50 |
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 53.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.6 | % | ASTM D638 |
| yield | 3.5 | % | ISO 527-2/50 |
| fracture | 7.3 | % | ASTM D638 |
| fracture | 8.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2770 | MPa | ASTM D790 |
| — | 2420 | MPa | ISO 178 |
| bending strength | |||
| — | 89.0 | MPa | ISO 178 |
| Yield, 50 mm span | 98.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 27 | J/m | ASTM D256 |
| 23℃ | 38 | J/m | ASTM D256 |
| -30℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 92.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 110 | ℃ | ASTM D1525 10 |
| B50 | 111 | ℃ | ISO 306 |
| B120 | 114 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 7.4E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 65.0 | ℃ | UL 746 |
| Electrical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm in oil | 29 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.70 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.020 | ASTM D150 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 725 | ℃ | |
| 2 mm | 725 | ℃ | |
| 3 mm | 725 | ℃ | |
| Extreme oxygen index | 30 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 65 to 85 | °C | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 240 to 270 | °C | |
| Barrel front temperature | 260 to 295 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Processing (melt) temperature | 260 to 295 | °C | |
| Mold temperature | 45 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |