| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-1 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD，3.2mm | 0.5 – 0.7 | % | SABIC method |
| Water absorption rate | |||
| 24hr | 0.01 | % | ASTM D570 |
| proportion | 1.13 | – | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 102 | ASTM D785 | |
| tensile strength | |||
| Fracture, Type I, 5 mm/min | 68 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 5 mm/min | 5 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 3500 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 77 | J/m | ASTM D256 |
| 23℃ | 93 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa，3.2 mm | 124 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 136 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Impact mechanical performance | 105 | ℃ | UL 746B |
| Electrical performance | 110 | ℃ | UL 746B |
| Non mechanical impact performance | 110 | ℃ | UL 746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dissipation factor | |||
| 100 MHZ | 0.001 | IEC 60250 | |
| 1 GHz | 0.002 | ASTM D150 | |
| Relative permittivity | |||
| 100 MHz | 2.7 | IEC 60250 | |
| 1 GHz | 2.7 | ASTM D150 | |
| Volume resistivity | 1.E+15 | ohms·cm | ASTM D257 |
| High voltage arc marking rate | |||
| PLC | 4 | PLC Code | UL 746A |
| Compared to the leakage tracing index | |||
| CTI | 2 | PLC Code | UL 746A |
| Hot wire ignition (HWI) | |||
| PLC 1 | ≥1.5 | mm | UL 746A |
| High Ampere Arc Ignition (HAI) | |||
| PLC 2 | ≥1.5 | mm | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| ≥0.71 mm | V-1 | Internal Method | |
| ≥2.50 mm | 5VA | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 105-110 | ℃ | |
| Drying time | 3-4 | hr | |
| Drying time, maximum | 8 | hr | |
| Recommended maximum moisture content | 0.02 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Front temperature of material barrel | 270 to 310 | °C | |
| Temperature in the middle of the barrel | 260 to 305 | °C | |
| Temperature at the rear of the barrel | 250 to 300 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 280 to 310 | °C | |
| Mold temperature | 75 to 105 | °C | |
| Back pressure | 0.3 to 0.7 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |