NORYL™ Resin V01550

About
NORYL V01550 is a 15 % short glass fibre reinforced, flame retardant material with a HDT/A of 130C according ISO 75. NORYL V01550 is V0 at 0.75 mm according UL94 and is halogen free according VDE/DIN 472 part 815. NORYL V01550 is designed for electronic and electrical applications.&&

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS
Material Status	Commercial: Active
Features	Halogen free,Flame Characteristics
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.25	g/cm³	ISO 1183
Melt Volume Rate
280℃，5 kg	7.00	cm³/10min
300℃，5 kg	10.0	cm³/10min
Shrinkage rate
MD	0.30 to 0.50	%	Internal Method
Water absorption rate
Saturation, 23 ℃	0.50	%
Equilibrium, 23 ℃, 50% RH	0.060	%

IMPACT	Nominal value	Unit
Charpy Unnotch Impact strength
Notched impact strength of cantilever beam
-30℃	45	kJ/m²
23℃	45	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed, 100 mm span	145	℃	ISO 75-2/Be
1.8 MPa, unannealed, 100 mm span	135	℃	ISO 75-2/Ae
Vicat Softening Temp
A50	160	℃	ISO 306/A50
B50	150	℃	ISO 306
B120	155	℃	ISO 306/B120
Ball pressure test
123~127℃	通过
145℃	通过
Linear coefficient of thermal expansion
MD：23~80℃	4.0E-5	1/℃
TD：23~80℃	6.0E-5	1/℃
Thermal conductivity coefficient	0.28	W/m/K	ISO 8302
Relative temperature index	50.0	℃	UL 746
Electrical performance	50.0	℃	UL 746
Impact mechanical performance	50.0	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.0E+15	ohms	IEC 60093
Volume resistivity	1.0E+15	ohms·cm	IEC 60093
Dielectric strength
0.8 mm in oil	33	kV/mm
1.6 mm in oil	26	kV/mm
3.2 mm in oil	16	kV/mm
Relative permittivity
50 Hz	3.10
60 Hz	3.10
1 MHz	3.00
Dissipation factor
50 Hz	5.0E-3
60 Hz	5.0E-3
1 MHz	3.0E-3
Compared to the leakage tracing index	250	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
0.75 mm	V-0
3.00 mm	5VA
Glowing wire flammability index
3.2 mm	960	℃	IEC 60695-2-12
Extreme oxygen index	32	%	ISO 4589-2

MECHANICAL	Nominal value	Unit	Test method
Ball hardness
H358/30	130	MPa	ISO 2039-1
Tensile modulus	2700	MPa	ISO 527-1-2
tensile strength
fracture	50.0	MPa	ISO 527-2/5
Tensile strain
fracture	5.0	%	ISO 527-2/5
Bending modulus	3000	MPa	ISO 178
bending strength	100	MPa	ISO 178
Taber abraser
1000 cycles, 1000 g, CS-17 wheels	50.0	mg	Internal Method

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	110 to 120	°C
Drying time	2.0 to 3.0	hr
Hopper temperature	80 to 100	°C
Barrel rear temperature	260 to 280	°C
Barrel middle temperature	280 to 300	°C
Barrel front temperature	300 to 320	°C
Nozzle temperature	280 to 300	°C
Processing (melt) temperature	300 to 320	°C
Mold temperature	100 to 130	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.