| NORYL RN0712 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 37% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0712 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High liquidity,Hydrolysis stability,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-1 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2470 | MPa | ASTM D638 |
| Tensile modulus | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 49.0 | MPa | ISO 527-2/50 |
| fracture | 50.0 | MPa | ASTM D638 |
| yield | 51.0 | MPa | ASTM D638 |
| yield | 47.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 10 | % | Internal Method |
| fracture | 7.0 | % | ISO 527-2/50 |
| yield | 3.0 | % | ISO 527-2/50 |
| yield | 3.5 | % | ASTM D638 |
| Bending modulus | 2250 | MPa | ISO 178 |
| 50 mm span | 2300 | MPa | ASTM D790 |
| bending strength | 77.0 | MPa | ISO 178 |
| bending strength | |||
| Fracture, 50 mm span | 82.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃，6.4mm | 49 | J/m | ASTM D256 |
| -30℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 87.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 105 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 110 | ℃ | ISO 306 |
| B120 | 112 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 7.4E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 2.91 | ASTM D150 | |
| Relative permittivity | |||
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 3.2E-3 | IEC 60250 | |
| 1 MHz | 3.2E-3 | ASTM D150 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 725 | ℃ | IEC 60695-2-13 |
| 2 mm | 725 | ℃ | IEC 60695-2-13 |
| 3 mm | 725 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 34 | % | ISO 4589-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| 280℃，2.16 kg | 22.0 | cm³/10min | ISO 1133 |
| Apparent viscosity of melt | |||
| 280℃，1500 sec^-1 | 95.0 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 50 to 70 | % | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 230 to 250 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 60 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |