| About |
|---|
| PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/V1 rated. RTI Elec/Imp/Str 95/80/95. Good flow. Suitable for E/E market indoor/outdoor applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Halogen free,Flame Characteristics,V-1,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Weathering resistance | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 46.9 | MPa | ASTM D638 |
| yield | 57.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| yield | 6.5 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2310 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 82.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 91 | J/m | ASTM D256 |
| 23℃ | 260 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Energy at Peak Load | 16.3 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 40.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 92.8 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 102 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 95.0 | ℃ | UL 746 |
| Strength mechanical performance | 95.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 3.1E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 18 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.66 | ASTM D150 | |
| 60 Hz | 2.66 | ASTM D150 | |
| 1 MHz | 2.57 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 6.0E-3 | ASTM D150 | |
| 60 Hz | 6.0E-3 | ASTM D150 | |
| 1 MHz | 2.6E-3 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 33 | % | ASTM D2863 |
| Radiation Plate Listing (UL) | YES |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 77 to 82 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 216 to 266 | °C | |
| Barrel middle temperature | 227 to 271 | °C | |
| Barrel front temperature | 238 to 277 | °C | |
| Nozzle temperature | 249 to 277 | °C | |
| Processing (melt) temperature | 249 to 277 | °C | |
| Mold temperature | 54 to 77 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. Type I, 2.0 in/min |
| 4. 0.10 in/min |
| 5. Tungsten Electrode |
| 6. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |