| About |
|---|
| Non-Halogenated flame retardant, flexible NORYL resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL 1581. Good processing performance by using standard extrusion equipment. UL1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 30 seconds | 91 | ASTM D2240 | |
| tensile strength | |||
| fracture | 22.0 | MPa | ISO 527-2/50 |
| fracture | 26.0 | MPa | UL 1581 |
| fracture | 23.0 | MPa | ASTM D638 |
| Fracture, 136 ℃ | 27.0 | MPa | UL 1581 |
| Tensile strain | |||
| fracture | 95 | % | ISO 527-2/50 |
| fracture | 190 | % | UL 1581 |
| fracture | 110 | % | ASTM D638 |
| Fracture, 136 ℃ | 130 | % | UL 1581 |
| Bending modulus | 390 | MPa | ISO 178 |
| 100 mm span | 390 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Pant tear resistance | 13.0 | N/mm | ISO 6383-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -40.0 | ℃ | ASTM D746 |
| UL temperature rating | 105 | ℃ | UL 1581 |
| Heat Deformation（121℃） | 15 | % | UL 1581 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.2E+16 | ohms | ASTM D257 |
| Volume resistivity | 5.1E+15 | ohms·cm | ASTM D257 |
| Relative permittivity | |||
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 4.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 6.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| VW-1 | Pass | UL 1581 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 200 to 240 | °C | |
| Barrel 3 zone temperature | 240 to 270 | °C | |
| Barrel 5 zone temperature | 240 to 270 | °C | |
| Melt temperature | 240 to 270 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 3. Type I, 2.0 in/min |
| 4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 6. 0.49 in/min |
| 7. 2.0mm wire with 0.12 mm x 20 stranded copper |
| 8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |