| About |
|---|
| Flexible, Ultra-violet stabilized and non-halogenated flame retardant extrusion grade intended for applications such as cable jacket in compliance with UL62. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C temperature rating as defined by UL 62 TPE category. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 10 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Deformation（121℃） | 10 | % | UL 1581 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.6E+16 | ohms | ASTM D257 |
| Volume resistivity | 5.1E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 2 mm in oil | 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 5.00 GHz | 2.60 | Internal Method | |
| Dissipation factor | |||
| 5 GHz | 2.0E-3 | Internal Method | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| VW-1 | Pass | UL 1581 | |
| Smoke density | ASTM E662 | ||
| Flame，0.5 mm plaque，Ds，max | 120 | ASTM E662 | |
| Non-Flame，0.5 mm plaque，Ds，max | 170 | ASTM E662 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 30 seconds | 81 | ASTM D2240 | |
| tensile strength | |||
| fracture | 22.0 | MPa | UL 1581 |
| fracture | 15.0 | MPa | ASTM D638 |
| Fracture, 136 ℃ | 23.0 | MPa | UL 1581 |
| fracture | 17.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 330 | % | UL 1581 |
| fracture | 250 | % | ASTM D638 |
| Fracture, 136 ℃ | 290 | % | UL 1581 |
| fracture | 260 | % | ISO 527-2/50 |
| Bending modulus | |||
| 100 mm span | 27.0 | MPa | ASTM D790 |
| — | 25.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 180 to 220 | °C | |
| Barrel 3 zone temperature | 220 to 250 | °C | |
| Barrel 5 zone temperature | 220 to 250 | °C | |
| Melt temperature | 220 to 250 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 3. Type I, 2.0 in/min |
| 4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 6. 0.49 in/min |
| 7. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 8. Plaque |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |