| 比重低，具有非常好的非卤化阻燃性能。 用于如插头，应变消除装置和连接器。 UL 94-V0性能良好，可加工性好。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Halogen free |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shaw’s A | 82 | ASTM D2240 | |
| tensile strength | |||
| Fracture, 50 mm/min | 10 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 50 mm/min | 115 | % | ISO 527 |
| Bending modulus | |||
| 12.50 mm/min | 130 | MPa | ISO 178 |
| tear strength | 17 | N/mm | ISO 6383 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Brittle temperature | <-40 | ℃ | ASTM D 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.2E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 2 mm in oil | 25 | kV/mm | IEC 60243-1 |
| Relative dielectric strength | |||
| 1 MHz | 2.7 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.004 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.05 | ASTM D792 | |
| Water absorption rate | |||
| 23℃，48hr | 0.1 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：24 hrs | 0.48 | % | ASTM D955 |
| TD：24 hrs | 1.09 | % | ASTM D955 |
| Melt Flow Rate | |||
| 210℃，5.0kg | 31 | g/10min | ASTM D1238 |
| 250℃，2.16kg | 33 | g/10min | ASTM D1238 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 94V-0 | 5 | mm | UL 94 |
| Smoke density | |||
| 0.5mm, no flame, Ds, maximum | 70 | ASTM E 662 | |
| 0.5mm patch, flame, Ds, maximum | 90 | ASTM E 662 | |
| Glowing wire flammability index | |||
| 850 ℃, passed through | 3 | mm | IEC 60695-2-12 |
| Glowing wire flammability index | |||
| 3.0 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 25 | % | ISO 4589 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 60 – 80 | °C | |
| Drying time | 4 – 6 | hrs | |
| Drying time (cumulative) | 8 | hrs | |
| Maximum water content | 0.01 | % | |
| Melt temperature | 220 – 250 | °C | |
| Nozzle temperature | 220 – 250 | °C | |
| Front Section Zone 3 Temperature | 220 – 250 | °C | |
| Temperature in Zone 2 of the middle section | 210 – 240 | °C | |
| Temperature in Zone 1 of the rear section | 180 – 220 | °C | |
| Mold temperature | 40 – 60 | °C | |
| Back pressure | 3 – 10 | MPa | |
| Screw speed | 30 – 80 | rpm | |
| Shoot to the size of the cylinder block | 30 – 70 | % | |
| Depth of exhaust groove | 0.03 – 0.05 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |