| About |
|---|
| GF-Reinforced / HB, Impact strength, GF 15%&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good flexibility,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：2.0 mm | 1.2 | % | |
| MD：2.0 mm | 0.60 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.090 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5200 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 5000 | MPa | ISO 178 |
| bending strength | 135 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 212 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 188 | ℃ | ISO 75-2/A |
| Melting temperature | 224 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：-30~50℃ | 6.0E-5 | 1/℃ | |
| MD：-30~120℃ | 6.0E-5 | 1/℃ | |
| MD：50~120℃ | 6.0E-5 | 1/℃ | |
| TD：-30~50℃ | 8.0E-5 | 1/℃ | |
| TD：-30~120℃ | 9.0E-5 | 1/℃ | |
| TD：50~120℃ | 1.0E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 4.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1 mm | 24 | kV/mm | |
| 2 mm | 21 | kV/mm | |
| Relative permittivity | |||
| 1 MHz | 3.20 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.020 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 5.0 to 8.0 | hr | |
| Barrel rear temperature | 240 | °C | |
| Barrel middle temperature | 245 | °C | |
| Barrel front temperature | 255 | °C | |
| Nozzle temperature | 255 | °C | |
| Mold temperature | 80.0 to 100 | °C | |
| Injection pressure | 20.0 to 150 | MPa | |
| Screw speed | 80 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |