| NOVALAST® 8001 is a Thermoplastic Vulcanizate (TPV) material. It is available in North America for blow molding, extrusion, or injection molding. Primary attribute of NOVALAST® 8001: Chemical Resistant.&& |
| Product Description | |
|---|---|
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Good coloring |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.963 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.5 to 2.0 | % | ASTM D955 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 11.4 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 590 | % | ASTM D412 |
| tear strength | 42.4 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395 | ||
| 25℃，22 hr | 30 | % | ASTM D395 |
| 70℃，22 hr | 44 | % | ASTM D395 |
| 100℃，22 hr | 55 | % | ASTM D395 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds | 80 | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -45.6 | ℃ | ASTM D746 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 199 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |