| About |
|---|
| Novalloy-B B5504是一种丙烯腈丁二烯苯乙烯 + PBT (ABS+PBT)产品,含有的填充物为20% 玻璃纤维增强材料。 它可以通过涂层或注射成型进行加工,在北美洲有供货。 Novalloy-B B5504的应用领域包括电气/电子应用、房屋、商业/办公用品 和 涂覆应用。 特性包括: 阻燃/额定火焰 Flame Retardant 耐化学品 耐磨 附着力强&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | ABS+PBT |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good Dimensional Stability,High elastic,Good liquidity,Flame Characteristics,High Heat Resistance,Good bond,Good wear resistance,Grease resistance,Solvent resistance,V-0,5VA |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.25 to 0.45 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 97.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 6470 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 142 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35 mm | 200 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.35 mm | 125 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.6E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 100 Hz | 3.60 | ASTM D150 | |
| Dissipation factor | |||
| 100 Hz | 3.0E-3 | ASTM D150 | |
| Arc resistance | |||
| 3.18 mm | 71.0 | sec | ASTM D495 |
| Compared to the resistance to leakage and marking index | |||
| 3.18 mm | 375 | V | UL 746 |
| High Arc Burning Index (HAI) (1.59 mm) | 39.0 | UL 746 | |
| High voltage arc marking rate (HVTR) (1.59 mm) | 183 | mm/min | UL 746 |
| Hot wire ignition (HWI) (1.59 mm) | 43 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | V-0 | UL 94 | |
| 2.90 mm, all colors | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 121 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Processing (melt) temperature | 241 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.483 to 1.45 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |