| About |
|---|
| Novalloy-C CE1810是一种聚碳酸脂 + 聚酯（PC+聚酯）材料,。 该产品在亚太地区有供货,。&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 63.0 | MPa | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 135 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 115 | ℃ | ISO 75-2/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Back pressure | 10.0 to 20.0 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |