| Novalloy-E E50是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在亚太地区有供货,。 Novalloy-E E50的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | ABS |
| Material Status | Commercial: Negative |
| Features | V-2,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 6.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 37.0 | MPa | ISO 527-2 |
| Bending modulus | 1800 | MPa | ISO 178 |
| bending strength | 56.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 6.0E+12 | ohms | ASTM D257 |
| Dielectric strength | |||
| 1.5 mm | 11 | kV/mm | ASTM D149 |
| Arc resistance | |||
| 3.0 mm | 57.0 | sec | ASTM D495 |
| 3.0 mm | PLC 7 | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 210 to 220 | °C | |
| Barrel front temperature | 220 to 230 | °C | |
| Nozzle temperature | 210 to 220 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 10.0 to 20.0 | MPa | |
| Screw speed | 60 to 90 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |