| About |
|---|
| Novalloy-S S69P1是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。 该产品在亚太地区有供货,。 Novalloy-S S69P1的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 11 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 64.0 | MPa | ISO 527-2 |
| Bending modulus | 2640 | MPa | ISO 178 |
| bending strength | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 102 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 220 to 260 | °C | |
| Barrel middle temperature | 240 to 270 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |