| About |
|---|
| Novamid®是高质量的聚酰胺，这条特殊的生产线主要是为满足日本客户的要求而设立的。&&Novamid®应用地域广，行业宽，种类多。从汽车到包装，Novamid®背后都有经验丰富的专家队伍进行支持。 |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Good stripping performance,Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt volume flow velocity | 39 / * | cm³/10min | ISO 1133 |
| temperature | 230 / * | °C | ISO 1133 |
| load | 2.16 / * | kg | ISO 1133 |
| Melt Index (MFI) | 40 / * | g/10min | ISO 1133 |
| MFI test temperature | 230 / * | °C | ISO 1133 |
| MFI testing load | 2.16 / * | kg | ISO 1133 |
| Shrinkage rate | |||
| TD | 1 / * | % | ISO 294-4 |
| Shrinkage rate | |||
| MD | 1.1 / * | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3600 / 1800 | MPa | ISO 527-1-2 |
| Yield stress | 80 / 50 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 4.8 / 17 | % | ISO 527-1/2 |
| Bending modulus | 3600 / 1800 | MPa | ISO 178 |
| bending strength | 120 / 55 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 220 / * | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 1.8 MPa | 70 / * | ℃ | ISO 75-1/2 |
| Hot deformation temperature | |||
| 0.45 MPa | 192 / * | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| TD | 0.6E-4 | /℃ | ISO 11359-1/-2 |
| Linear coefficient of thermal expansion | |||
| MD | 0.7E-4 | /℃ | ISO 11359-1/-2 |
| Combustibility at a thickness of h | V-0 / * | class | IEC 60695-11-10 |
| The thickness of the test specimen used for testing | 0.75 / * | mm | IEC 60695-11-10 |
| UL certification | Yes / * | – | – |
| Glow wire combustion index GWFI | 960 / – | °C | IEC 60695-2-12 |
| GWFI (thickness (1)) | 3 / – | mm | IEC 60695-2-12 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100 Hz | 4 / – | IEC 60250 | |
| Relative permittivity | |||
| 1 MHz | 4 / – | IEC 60250 | |
| Dissipation factor | |||
| 100 Hz | 100 / – | E-4 | IEC 60250 |
| Dissipation factor | |||
| 100 Hz | 200 / – | E-4 | IEC 60250 |
| Volume resistivity | 1E15 | ohms·cm | IEC 60093 |
| Dielectric strength | 26 / – | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 550 / – | V | IEC 60112 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Moisture absorption rate | 2.6 / * | % | Sim. to ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 90 / N | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 3 / 10 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |