| About |
|---|
| PF-0218-B (750 ppm Slip, 3150 ppm Antiblock): Trash bags, liners, general packaging PF-0218-D (1500 ppm Slip, 6300 ppm Antiblock): Industrial liners, heavy duty bags PF-0218-F (Process antioxidant only): Stretch wrap, blend resin, industrial packaging&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 190 | MPa | ASTM D882 |
| 1% secant, MD, 25 µ m, blow molded film | 170 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| TD, yield, 25 µ m, blow molded film | 10.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 32.0 | MPa | ASTM D882 |
| MD, yield, 25 µ m, blow molded film | 10.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 700 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 660 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 100 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 330 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 110 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 43 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 14 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| Blow molded film, 25.0 µ m | 290 | J/cm | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |